Light-Color Conduction Pigment B0₁ is on the basic of light-colored inert material. After surface coating andse miconductor doped processing, it generates conductive oxide cover on the surface of basic material, and then get a new conduction ligth-colored pigments, they are compared with similar products have the following advantages:
1.Outstanding electrical conductivity even at a lower addition level of pigments.
2.Excellent electrical conductivity even in the crosslinking system containing other pigments and fillers.
3.When mixed with other pigments, a colorful conductive coatings can be formulated.
4.High durabiltiy in conductivity of coating film.
5.it can be widely used in the industries of coatings, printing inks and plastics to expand the applications of these products and enhance the added value of products.

Product Performance:
1.components: Mica-snO₂
2.appearance: light dark
3.resistivity in powder Ω.cm 200
4.heat-resistan ℃， 400
5.Oil absorption: 60-80
6.Fieness: 25
Recommended formula and Technology in producing anti-static Pain:

1.Mixture A:
Epoxy resin paste(S=85%) 52
Mixed solvents 23.7
Anti-static light-colored powder 23.6
BYK 163 0.7
2.Mixture B:
polyamide(S=95%) 63
Mixed solvents 37
3.Paints process:
(1)Milling paste
(2)Mixture A being produced
A.Added mixed solvents, BYK 163 in paint drums and mixed
B.Added the anti-static light-colored powder gradually,stirring to slow or hand-stirring,Wet up the materials and form a wet paste.
C.color paste by adding(fineness of less than 50 microns),high-speed dispersion 15min
(3)Mixture B being produced(home made)
4.Paint materials ratio:
Mixture A:Mixture B=5:1
5.Composition of the pains

6.Technical Data:
Paint film color and appearance: all colors, smooth film
Viscosity(DNJ-79 type)，mpa.s 100-300
Dry time(surface dired)hr 4
(solid dried),hr 24
Resistance on the surface, 104-107
Flexibility,mm 1
Impact strength,cm 50
Adhesion, grade 2